Silicon Bronze - Bare (AWS ERCuSi-A)
Recommended for Inert gas arc welding of copper, copper-silicon and

copper-zinc base metals to themselves and to steel. Excellent for plain

or galvanized steel metal or other coated steel.  Also used for surfacing

areas subjected to corrosion.

Melting point : 1018°C
Chemical (%) : Cu 94min, Si 2.8~4.0, 
                      Mn 0.5~1.5

Tensile Strength (min) : 50,000 psi

Phos-Bronze - Bare (AWS ERCuSn-C)
Recommended for surfacing applications which requires great hardness and high tensile strength. This alloy is commonly used for joining brass alloys and cast iron to carbon steel.

Melting Point : 1000°C
Chemical (%) : Cu 90min, Sn 7~9,
                         P 0.1~0.3, Zn 0.2
Tensile Strength (min) : 60,000 psi

Low Fuming Bronze - Bare (AWS RBCuZn-C)
Recommended for general purpose repair work on steel, cast iron and other copper base alloys. The porosity-free deposits yield excellent colour match to the yellow brasses.

Melting point : 865 - 890°C
Chemical (%) : Cu 57~59, Sn 0.8~1.0, 
                         Fe 0.35~1.2, Si 0.05~0.15, 
                         Mn 0.03~0.1, Zn Bal
Tensile Strength (min) : 50,000 psi

Nickel Silver - Bare (AWS RBCuZn-D)
Recommended for applications requiring higher mechanical properties and situations where good colour match is important. This alloy is primarily intended for braze welding steel and cast iron.

Melting Point : 920~930°C
Chemical (%) : Cu46~50, Ni 9~11, 
                        Si 0.04~0.25, Zn Bal
Tensile Strength (min) : 60,000 psi

Sizes available :
Cut Rods :
Dia. : 1.6mm (1/16"), 2.0mm (0.08"), 2.4mm (3/32"),
         3.2mm (1/8"), 4.0mm (5/32")
Lth. : 14", 18", 36"  or 500mm, 1,000mm

Spooled wire :
Dia. 0.8mm (0.03"), 0.9mm (0.035"), 1.2mm (0.045"), 1.6mm (1/16")